슬러리 코팅 공정으로 제조된Fe 폼의 기공 특성에 미치는 Fe및 Fe2O3 분말의 혼합 비율의 영향

서지정보

ㆍ발행기관 : 한국분말야금학회 ㆍ수록지정보 : 한국분말야금학회지 / 21권 / 4호
ㆍ저자명 : 최진호, 정은미, 박다희, 양상선, 한유동, 윤중열

목차

Abstract
1. 서 론
2. 실험방법
3. 결과 및 고찰
4. 결 론
감사의 글
참고문헌

영어 초록

Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction ofpores. In particular, open, penetrating pores are necessary for industrial applications such as in high temperature filtersand as a support for catalysts. In this study, Fe foam with above 90% porosity and 2 millimeter pore size was suc-cessfully fabricated by a slurry coating process and the pore properties were characterized. The Fe and Fe2O3 powdermixing ratios were controlled to produce Fe foams with different pore size and porosity. First, the slurry was preparedby uniform mixing with powders, distilled water and polyvinyl alcohol(PVA). After slurry coating on the polyure-thane(PU) foam, the sample was dried at 80℃. The PVA and PU foams were then removed by heating at 700℃ for 3hours. The debinded samples were subsequently sintered at 1250℃ with a holding time of 3 hours under hydrogenatmosphere. The three dimensional geometries of the obtained Fe foams with an open cell structure were investigatedusing X-ray micro CT(computed tomography) as well as the pore morphology, size and phase. The coated amount ofslurry on the PU foam were increased with Fe2O3 mixing powder ratio but the shrinkage and porosity of Fe foams weredecreased with Fe2O3 mixing powder ratio.

참고 자료

없음