인 함유 벤조산 변성폴리에스테르의 합성과 이를 이용한 PU 난연도료의 도막물성 연구
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2005.06
- 13페이지/ 어도비 PDF
- 가격 4,500원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국유화학회
ㆍ수록지정보 : 韓國油化學會誌 / 22권 / 2호
ㆍ저자명 : 박홍수, 심일우, 조혜진, 유혁재, 김명수, 함현식
영어 초록
Reaction intermediates PCP/BZA (PBI) and tetramethylene bis(orthophosphate)(TBOP) were synthesized from polycaprolactone (PCP) and benzoic acid (BZA) and from pyrophosphoric acid and 1,4-butanediol, respectively. Benzoic acid modified polyesters containing phosphorus (APTB-S, -10, -15) were synthesized by polycondensation of the prepared PBI (containing 5, 10, 15wt% of benzoic acid), TBOP, adipic acid, and 1,4-butanediol. Network structured PU flame-retardant coatings (APHD) were prepared by curing the synthesized benzoic acid modified polyesters containing phosphorus (APT B - 5 , -10, -15) with hexamethylene diisocyanate (HDI)-timer. From the TGA analysis of APTBs, it was found that the afterglow decreased with the amount of BZA content at the high temperatures. With the introduction of BZA, the film viscosity and film hardness of APHD decreased. With the introduction of caprolactone group, the flexibility, impact resistance, accelerated weathering resistance of APTBs increased. Flame retardancy of the coatings was tested. In a vertical burning method, APHD shows 210~313 seconds, which indicates that the coatings are good flame-retardant coatings. Moreover, the amount of afterglow and flame retardancy of the coatings are decreased with increasing BZA content.
참고 자료
없음
"韓國油化學會誌"의 다른 논문
더보기 (5/10)