백색 LED용 청록색 BaSi2O2N2:Eu2+ 형광체의 합성 및 응용
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2011.05
- 5페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 21권 / 5호
ㆍ저자명 : 지순덕, 최강식, 최경재, 김창해
영어 초록
We have synthesized bluish-green, highly-efficient BaSi2O2N2:Eu2+ and (Ba,Sr)Si2O2N2:Eu2+ phosphors through aconventional solid state reaction method using metal carbonate, Si3N4, and Eu2O3 as raw materials. The X-ray diffraction (XRD)pattern of these phosphors revealed that a BaSi2O2N2 single phase was obtained. The excitation and emission spectra showedtypical broadband excitation and emission resulting from the 5d to 4f transition of Eu2+. These phosphors absorb blue light ataround 450nm and emit bluish-green luminescence, with a peak wavelength at around 495 nm. From the results of anexperiment involving Eu concentration quenching, the relative PL intensity was reduced dramatically for Eu=0.033. A smallsubstitution of Sr in place of Ba increased the relative emission intensity of the phosphor. We prepared several white LEDsthrough a combination of BaSi2O2N2:Eu2+, YAG:Ce3+, and silicone resin with a blue InGaN-based LED. In the case of onlythe YAG:Ce3+-converted LED, the color rendering index was 73.4 and the efficiency was 127lm/W. In contrast, in theYAG:Ce3+ and BaSi2O2N2:Eu2+-converted LED, two distinct emission bands from InGaN (450nm) and the two phosphors (475-750nm) are observed, and combine to give a spectrum that appears white to the naked eye. The range of the color renderingindex and the efficiency were 79.7-81.2 and 117-128 lm/W, respectively. The increased values of the color rendering indexindicate that the two phosphor-converted LEDs have improved bluish-green emission compared to the YAG:Ce-converted LED.As such, the BaSi2O2N2:Eu2+ phosphor is applicable to white high-rendered LEDs for solid state lighting.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (3/8)