BCTZ첨가가 NKLN-AS계 압전세라믹스의 미세구조와 압전/유전특성 및 상전이현상에 미치는 효과
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2012.01
- 7페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 22권 / 1호
ㆍ저자명 : 이웅재, 어순철, 이영근, 윤만순
영어 초록
Presently, the most promising family of lead-free piezoelectric ceramics is based on K0.5Na0.5NbO3(KNN). Lithium, silver and antimony co-doped KNN ceramics show high piezoelectric properties at room temperature, but often suffer from abnormal grain growth. In the present work, the (Ba0.85Ca0.15)(Ti0.88Zr0.12)O3 component, which has relaxor ferroelectric characteristics, was doped to suppress the abnormal grain growth. To investigate this effect, Lead-Free 0.95(K0.5Na0.5)0.95Li0.05NbO3-(0.05-x)AgSbO3-x(Ba0.85Ca0.15)(Ti0.88Zr0.12)O3[KNLN-AS-xBCTZ] piezoelectric ceramics were synthesized by ball mill and nanosized-milling processes in lead-Free 0.95(K0.5Na0.5)0.95Li0.05NbO3-(0.05-x)AgSbO3 in order to suppress the abnormal grain growth. The nanosized milling process of calcined powders enhanced the sintering density. The phase structure, microstructure, and ferroelectric and piezoelectric properties of the KNLN-AS ceramics were systematically investigated. XRD patterns for the doped and undoped samples showed perovskite phase while tetragonality was increased with increasing BCZT content, which increase was closely related to the decrease of TO-T. Dense and uniform microstructures were observed for all of the doped BCZT ceramics. After the addition of BCTZ, the tetragonal-cubic and orthorhombic-tetragonal phase transitions shifted to lower temperatures compared to those for the pure KNNL-AS. A coexistence of the orthorhombic and tetragonal phases was hence formed in the ceramics with x = 0.02 mol at room temperature, leading to a significant enhancement of the piezoelectric properties. For the composition with x = 0.02 mol, the piezoelectric properties showed optimum values of: d33 = 185 pC/N, kp = 41%, Tc=325˚C, TO-T=-4˚C.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (3/8)