In Vitro and In Vivo Evaluation of Composite Scaffold of BCP, Bioglass and Gelatin for Bone Tissue Engineering
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2014.06
- 9페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 24권 / 6호
ㆍ저자명 : Kim, Woo Seok, Nath, Subrata Deb, Bae, Jun Sang, Padalhin, Andrew, Kim, Boram, Song, Myeong Jin, Min, Young Ki
영어 초록
In this experiment, a highly porous scaffold of biphasic calcium phosphate (BCP) was prepared using the spongereplica method. The BCP scaffold was coated with 58S bioactive glass (BG) and sintered for a second time. The resulting scaffold was coated with gelatin (Gel) and cross-linked with [3-(3-dimethyl aminopropyl) carbodiimide] and N-Hydroxysuccinamide (EDC-NHS). The initial average pore size of the scaffold ranged from 300 to 700μm, with more than 85 % porosity. The coating of BG and Gel had a significant effect on the scaffold-pore size, decreasing scaffold porosity while increasing mechanical strength. The material and surface properties were evaluated by means of several experiments involving scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) and X-ray diffraction (XRD). Cytotoxicity was evaluated using MTT assay and confocal imaging of MC3T3-E1 pre-osteoblast cells cultured in vitro. Three types of scaffold (BCP, BCP-BG and BCP-BG-Gel) were implanted in a rat skull for in vivo evaluation. After 8 weeks of implantation, bone regeneration occurred in all three types of sample. Interestingly, regeneration was found to be greater (geometrically and physiologically) for neat BCP scaffolds than for two other kinds of composite scaffolds. However, the other two types of scaffolds were still better than the control (i.e., defect without treatment).
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (2/7)