Hydrogen Reduction of NiO Particles in a Single-Stage Fluidized-Bed Reactor without Sticking
(주)코리아스칼라
- 최초 등록일
- 2016.06.04
- 최종 저작일
- 2016.02
- 5페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 26권 / 2호
ㆍ저자명 : Chang-Sup Oh, Hang Goo Kim, Yong Ha Kim
목차
1. Introduction
2. Experimental
3. Results and Discussion
4. Conclusion
Acknowledgments
References
영어 초록
A commercial NiO (green nickel oxide, 86 wt% Ni) powder was reduced using a batch-type fluidized-bed reactor in a temperature range of 500 to 600 oC and in a residence time range of 5 to 90 min. The reduction rate increased with increases in temperature; however, agglomeration and sintering (sticking) of Ni particles noticeably took place at high temperatures above 600 oC. An increasing tendency toward sticking was also observed at long residence times. In order to reduce the oxygen content in the powder to a level below 1 % without any sticking problems, which can lead to defluidization, proper temperature and residence time for a stable fluidized-bed operation should be established. In this study, these values were found to be 550 oC and 60 min, respectively. Another important condition is the specific gas consumption rate, i.e. the volume amount (Nm3) of hydrogen gas used to reduce 1 ton of Green NiO ore. The optimum gas consumption rate was found to be 5,000 Nm3/ton-NiO for the complete reduction. The Avrami model was applied to this study; experimental data are most closely fitted with an exponent (m) of 0.6 ± 0.01 and with an overall rate constant (k) in the range of 0.35~0.45, depending on the temperature.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (2/7)