부식피로에 의한 선박용 알루미늄 합금제 용접부의 균열 전파기동에 관한 연구
(주)코리아스칼라
- 최초 등록일
- 2023.04.05
- 최종 저작일
- 1988.12
- 8페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국수산해양기술학회(구 한국어업기술학회)
ㆍ수록지정보 : 수산해양기술연구 / 24권 / 4호
ㆍ저자명 : 임우조, 이진열
영어 초록
Recently with the rapid development in marine and shipbuilding industries such as marine structures, ships and chemical plants, it takes much interest in the study of corrosion fatigue characteristics that was close up an important role in mechanical design. In this study, characteristics of corner crack propagation on the base metal and heat affected zone of 5086 Al-Alloy was tested by using of a rotary bending fatigue tester and was investigated under the environments of specific resistance, σ=25Ω cm and air. The corrosion fatigue crack initiation and corrosion fatigue life sensitivity were quantitatively inspected for 5086 Al-Alloy in the specific resistance, σ=25Ω cm. Main results obtained are as follows: (1) The corrosion sensitivity of heat affected zone under specific resistance, σ=25Ωcm shows approximately 1.69~2.22 and corrosion sensitivity of base metal is more susceptible than that of heat affected zone. (2) The corrosion fatigue life sensitivity on heat affected zone decreases eminently than that of initial corrosion fatigue crack. (3) The characteristics of quarter elliptical corner crack propagation shows that depth crack is more grown than surface crack at crack initiation, but the surface crack is more propagated than depth crack as the crack propagation is increased. (4) The surface crack and depth crack growth on heat affected zone by softness show delayed phenomenon than that of base metal.
참고 자료
없음
"수산해양기술연구"의 다른 논문
더보기 (1/6)