Fabrication of isotropic bulk graphite using artificial graphite scrap
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 15권 / 2호
ㆍ저자명 : Sang-Min Lee, Dong-Su Kang, Woo-Seok Kim, Jea-Seung Roh
ㆍ저자명 : Sang-Min Lee, Dong-Su Kang, Woo-Seok Kim, Jea-Seung Roh
목차
1. Introduction2. Experimental Procedure
3. Results and Discussion
4. Conclusions
Acknowledgments
References
한국어 초록
Isotropic synthetic graphite scrap and phenolic resin were mixed, and the mixed powder was formed at 300 MPa to produce a green body. New bulk graphite was produced by carbonizing the green body at 700°C, and the bulk graphite thus produced was impregnated with resin and re-carbonized at 700°C. The bulk density of the bulk graphite was 1.29 g/cm3, and the porosity of the open pores was 29.8%. After one impregnation, the density increased to 1.44 g/cm3 while the porosity decreased to 25.2%. Differences in the pore distribution before and after impregnation were easily confirmed by observing the microstructure. In addition, by using an X-ray diffractometer, the degrees-of-alignment (Da) were obtained for one side perpendicular to the direction of compression molding of the bulk graphite (the “top-face”), and one side parallel to the direction of compression molding (the “side-face”). The anisotropy ratio calculated from the Da-values obtained was 1.13, which indicates comparatively good isotropy.영어 초록
Isotropic synthetic graphite scrap and phenolic resin were mixed, and the mixed powder was formed at 300 MPa to produce a green body. New bulk graphite was produced by carbonizing the green body at 700°C, and the bulk graphite thus produced was impregnated with resin and re-carbonized at 700°C. The bulk density of the bulk graphite was 1.29 g/cm3, and the porosity of the open pores was 29.8%. After one impregnation, the density increased to 1.44 g/cm3 while the porosity decreased to 25.2%. Differences in the pore distribution before and after impregnation were easily confirmed by observing the microstructure. In addition, by using an X-ray diffractometer, the degrees-of-alignment (Da) were obtained for one side perpendicular to the direction of compression molding of the bulk graphite (the “top-face”), and one side parallel to the direction of compression molding (the “side-face”). The anisotropy ratio calculated from the Da-values obtained was 1.13, which indicates comparatively good isotropy.참고 자료
없음태그
"Carbon Letters"의 다른 논문
- Effects of carbonization temperature on pore developmen..5페이지
- Facile preparation of self-assembled wool-based graphen..6페이지
- Preparation of pitch from pyrolized fuel oil by electro..7페이지
- Effect of stacking sequence on the flexural and fractur..4페이지
- Study on lowering the percolation threshold of carbon n..8페이지
- Study on electrochemical performances of sulfur-contain..4페이지
- Removal of methylene blue using lemon grass ash as an a..8페이지
- Superhydrophobic carbon-based materials: a review of sy..16페이지
- Double-walled carbon nanotubes: synthesis, structural c..12페이지
- My life and Korean carbon society4페이지