10 wt%, 20 wt%Li-TiO2 복합분말의 합성과 광촉매 활성평가
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국분말야금학회
ㆍ수록지정보 : 한국분말야금학회지 / 23권 / 1호
ㆍ저자명 : 김형철, 한재길
ㆍ저자명 : 김형철, 한재길
한국어 초록
10 wt.% and 20 wt.%Li-TiO2 composite powders are synthesized by a sol-gel method using titanium isopropoxide and Li2CO3 as precursors. The as-received amorphous 10 wt.%Li-TiO2 composite powders crystallize into the anatase-type crystal structure upon calcination at 450oC, which then changes to the rutile phase at 750oC. The asreceived 20 wt%Li-TiO2 composite powders, on the other hand, crystallize into the anatase-type structure. As the calcination temperature increases, the anatase TiO2 phase gets transformed to the LiTiO2 phase. The peaks for the samples obtained after calcination at 900oC mainly exhibit the LiTiO2 and Li2TiO3 phases. For a comparison of the photocatalytic activity, 10 wt.% and 20 wt.% Li-TiO2 composite powders calcined at 450oC, 600oC, and 750oC are used. The 20 wt.%Li-TiO2 composite powders calcined at 600oC show excellent efficiency for the removal of methylorange영어 초록
10 wt.% and 20 wt.%Li-TiO2 composite powders are synthesized by a sol-gel method using titanium isopropoxide and Li2CO3 as precursors. The as-received amorphous 10 wt.%Li-TiO2 composite powders crystallize into the anatase-type crystal structure upon calcination at 450oC, which then changes to the rutile phase at 750oC. The asreceived 20 wt%Li-TiO2 composite powders, on the other hand, crystallize into the anatase-type structure. As the calcination temperature increases, the anatase TiO2 phase gets transformed to the LiTiO2 phase. The peaks for the samples obtained after calcination at 900oC mainly exhibit the LiTiO2 and Li2TiO3 phases. For a comparison of the photocatalytic activity, 10 wt.% and 20 wt.% Li-TiO2 composite powders calcined at 450oC, 600oC, and 750oC are used. The 20 wt.%Li-TiO2 composite powders calcined at 600oC show excellent efficiency for the removal of methylorange참고 자료
없음"한국분말야금학회지"의 다른 논문
- Kinetic Spray 공정을 이용한 벌크형 탄탈륨 소재의 제조 및 미세조직/물성7페이지
- Kinetic Spray 공정으로 제조된 Nb 코팅 소재의 미세조직 및 물성에 미치는 열간 등압 성..6페이지
- 저온분사법에 의해 제조된 Cu-Ga 타겟의 스퍼터링 특성평가5페이지
- Development of Powder Injection Molding Process for Fab..7페이지
- 코어-쉘 구조를 갖는 BaTiO3@Fe 나노섬유의 합성 및 전자파 흡수 특성5페이지
- 실리콘 wafer sludge로부터 얻어진 SiC의 단광화 기술6페이지
- CuO-SnO2/camphene 슬러리의 동결 및 소결조건이 Cu-Sn 다공체의 기공구조에 미치는 ..5페이지
- 기계적 밀링공정에 의한 은 플레이크 분말 제조7페이지
- Fe 및 Ni기 산화물 분산 강화 합금의 연구동향8페이지
- 펄스전류활성소결법을 이용한 스퍼터링 타겟용 Cu-Mn 소결체 제조 및 특성평가7페이지